Everlube氟素/二硫化钼涂层

Everlube

MoS2/PTFE, Solid Film Lubricant

一、产品说明Product Description

Everlube 6111为热固化、溶剂基础型，含有高分子树脂粘合剂的氟素/二硫化钼涂层。此涂层系为提供高腐蚀性及超低摩擦系数用途使用。高抗剥裂及抗摩擦特性。详细规范也可参考我司网站Everlube 6111 is a thermally cured, PTFE/MoS2 based solid film lubricant with a high molecular weight　epoxy binder system. This coating is ideal for application which require excellent corrosion resistance　along with a very low cofficient of friction. Everlube 6111 also offers very good chip and wear resistance.For specifications on Everlube 6111, please visit our specification guide at:　http://www.everlubeproducts.com/products

二、特性 / 优点Features / Benefits

卓越的抗腐蚀性Superior corrosion resistance

高抗磨特性　Very good wear resistance

抗剥裂及摩擦性 Excellent chip and abrasion resistance

适合用于低负载用途Ideal for lighter load carrying applications.

三、市场Markets 用途Typical Applications

螺丝行业Fasteners

金属组合工件 Fabricated Metal Parts

工业机械 Industrial Machinery

化工业Chemical Processing

大螺丝扣件Large Fasteners

弹簧，线圈，夹钳Springs, coils, and clamps

心轴，铸件，冲压件Mandrels, castings, and stampings

石化行业五金工件Petro chem. hardware

四、物性特性Physical Properties

固体润滑剂Lubricating Solids: 二硫化钼　＋　氟素　　MoS2 + PTFE

粘合剂Binder: 高分子树脂　High Molecular Weight Epoxy

颜色及外观Color and Appearance:* 深灰色Dark Gray finish

附载体Carrier: 溶剂 Solvent borne

固体含量(重量比) Solids (by weight):* 34% to 38%

密度Density:* 8.7 ± 0.5 lb/gal (1042 ± 60 grams/liter)

闪火点Flash Point: 25°F (-4°C)

有机溶剂含量Volatile Organic Compound: 685 grams/liter (5.71 lb/gal)

涂布面积理论值Theoretical Coverage:1 744 ft2/gal @ 0.5 mils (18.2 m2/liter @ 12.7 microns)

替换或修补涂层Alternative or Repair Coatings: 修补用途　Perma-Slik RMT 相容

五、加工信息 Processing Information

干膜厚度Dry Film Thickness 0.02 to 0.07 mils (1 to 2 microns)

稀释 / 清洗溶剂Dilution/Cleanup Solvent: MEK　

稀释比例Dilution Ratio: 产品对溶剂比1:1 (Product to Solvent) 数量比

六、固化时间Cure Cycle:         

1小时＠190° C

1 hr. @ 375° F 

建议预表面处理方式Suggested Pretreatment:  喷砂 或磷酸皮膜 处理Grit blast or Phosphate

建议涂布方式Suggested Application Methods:  喷涂Spray

请参照加工工艺说明书 #3000-A　

For additional (general) process information, please see Processing Bulletin #3000-A