Everlube高富锌涂层 

Ever-Slik  1236

富锌涂层  Zinc Rich Barrier Coating

一、产品说明Product Description

Ever-Slik 1236为热固化、溶剂基础型，含有有机金属树脂的高富锌涂层。此涂层系研发为提供更具有卓越的抗腐蚀性保护，并广泛应用于各种用途。Ever-Slik 1236可做为单一产品使用，也可使用为基底涂层搭配其它Everlube产品做为更进一步抗腐蚀保护或特殊用途使用。详细规范也可参考我司网站Ever-Slik 1236 is a thermally cured, solvent-based, zinc rich coating with an organo-metallic binder system. This coating was developed to provide superior corrosion protection in a wide variety of applications. Ever-Slik 1236 may be used as a stand-alone coating; or it can be used as a primer for other Everlube Products functional coatings to achieve an excellent combination of corrosion resistance and other specific functionality. Specifications for this product can be found at http://www.everlubeproducts.com/products.

特性 / 优点Features / Benefits

卓越的抗腐蚀性Superior corrosion resistance

干膜含锌量超过80% Dry film contains >80% zinc

高抗化学性Good chemical resistance

简易涂层可用喷雾或浸泡方式Excellent results when sprayed or bulk coated

二、市场Markets 用途Typical Applications

汽车Automotive

工业机械及设备Industrial machinery & equipment

金属工件Fabricated metal parts

航空 / 国防Aerospace/defense

螺丝扣件Fasteners

齿轮、齿条、轨道Gears, splines, and rails

阀门、组件、连接头Valves, fittings, and connectors

工具、五金件等Tools, misc. hardware

三、物性特性Physical Properties

固体润滑剂Lubricating Solids: 无N/A

粘合剂Binder: 有机金属 Organo-metallic

颜色及外观Color and Appearance:* 雾银色Matte silver finish

附载体Carrier: 溶剂 Solvent borne

固体含量(重量比) Solids (by weight):* 58% to 62%

密度Density:* 12.0 ± 0.5 lb/gal (1439 ± 60 grams/liter)

闪火点Flash Point: 99°F (37°C)

有机溶剂含量Volatile Organic Compound: 560 grams/liter (4.67 lb/gal)

涂布面积理论值Theoretical Coverage:1 1060 ft2/gal @ 0.5 mils (26.0 m2/liter @ 12.7 microns)

替换或修补涂层Alternative or Repair Coatings: 无 N/A

四、加工信息 Processing Information

干膜厚度Dry Film Thickness 0.3 to 0.7 mils (7 to 18 microns)

稀释 / 清洗溶剂Dilution/Cleanup Solvent: 庚烷 、甲烷、甲苯、石油醚等有机溶剂Heptane, Toluene, or RAC Solvent. Xylene or VM&P mineral spirits may be used as a retarder solvent.

稀释比例Dilution Ratio: 喷涂使用For Spray: 10% to 20% by volume (or as needed)

浸泡使用For Dip/Spin: 5% to 10% by volume (or as needed)

五、固化时间Cure Cycle:         

热风循环烤箱Air circulated oven:

输送带式烤箱 Conveyer Oven: 

25 分钟minutes @ 300°F ± 25°F (149°C)

15 分钟minutes @ 350°F ± 25°F (177°C)

建议预表面处理方式Suggested Pretreatment:  喷砂 或磷酸锌 处理Grit blast, Zinc Phosphate

建议涂布方式Suggested Application Methods: 浸泡 喷涂Dip spin, spray

未干固化的表面非常具有水敏感性，水污染有可能会降低涂层效果，请参照加工工艺说明书 #3000-A 。Uncured coating is moisture sensitive. Water contamination may reduce the effectiveness of the coating   For additional (general) process information, please see Processing Bulletin #3000-A